Page 6 - Industrial Coatings

POLYCOAT POLYEURO® 5502F
PRODUCTS (POLYEURO® 5510)

A Division of American Polymers Corp. Two Component Aromatic
Polyurea Protective Coating

DESCRIPTION TECHNICAL DATA
Polyeuro® 5502F is a fast set, rapid curing, 100% solids, Mix Ratio by Volume .......................................... 1A : 1B
flexible, aromatic, two component spray polyurea that can be Pot Life ............................................................... 2-4 seconds
applied to suitably prepared concrete and metal surfaces. Its Tack Free Time ................................................... 15-20 secs
extremely fast gel time makes it suitable for applications Recoat Time ........................................................ 0-6 hours
down to -20°F. It may be applied in single or multiple Viscosity at 150-160°F (66.5-71°C), Brookfield:
applications without appreciable sagging and is relatively Part-A ................................................................. 50 ± 20 cps
insensitive to moisture and temperature allowing application Part-B ................................................................. 50 ± 20 cps
in most temperatures. Density (Side A & B Combined) ........................ 8.75 lbs/gal
Flash Point .......................................................... >200°F
FEATURES Hardness, ASTM D-2240 .................................. 50 ± 5 D
Tensile, ASTM D-412* ........................................ 2800 ± 300 psi
Zero VOC (100% Solids)  Seamless Elongation, ASTM D-412* .................................. 375% ± 50%
Tear, ASTM D-412* ............................................ 450 ± 50 pli
Excellent Thermal Stability  Odorless Service Temperature ......................................... -40°F to 250°F
Water Vapor Permeability ASTM E-96 .............. 0.00042
No Toxic Vapors Non-Reactive
(*These physical properties from sample sprayed with EXP-2 @ 2000
Meets USDA Criteria psi minimum, with Gusmer GX7-400 mechanical purge gun @ 150-
160°F. Different machine and parameter will change these
Low Temperature Flexibility properties. User should perform their own independent testing as
properties are approximate.)
Good Chemical Resistance

Coats Carbon or Mild Steel Metals without Primer

Installed With or Without Reinforcement in Transitional

Areas

TYPICAL USES SURFACE PREPARATION
In general, coating performance and adhesion are directly
Airports Power Plants proportional to surface preparation. Most failures in the
performance of surface coatings can be attributed to poor
Refineries Structural Steel surface preparation. Polyurea coatings rely on the structural
strength of the substrate to which they are applied. All sur-
Fertilizer Plants Warehouse Floors faces must be free of dust, dirt, oil, grease, rust, corrosion and
other contaminants. When coating substrates previously
Mining Operations Cold Storage Facilities used, it is important to consider the possibility of substrate
absorption, which may affect the adhesion of the coating
Food Processing Plants Landfill Containment system, regardless of the surface preparation. Polycoat
recognizes the potential for unique substrates from one
Marine Environments Paper and Pulp Mills project to another. The following information is for general
reference, and for project-specific questions, contact Polycoat.
Secondary Containment Parking Garage Decks New and Old Concrete:
Refer to SSPC-SP13/NACE 6, or ICRI 03732: CSP 3-5. New
Walkways and Balconies concrete must be cured for 28 days prior to product applica-
tion. Surface must be clean, dry, sound and offer sufficient
Water and Waste Water Treatment rofile for product adhesion. Remove all dust, dirt, oil, form release
agents, curing compounds, salts, efflorescence, laitance and other
Industrial and Manufacturing Facilities foreign matter by shotblasting and/or suitable chemical means, in
accordance with local chemical regulations. Rinse thoroughly, to
COLORS achieve a pH between 8.0 and 11.0. Allow to dry completely. If old
Neutral. Custom colors are available upon request. concrete has a surface that has deteriorated to an unacceptably
rough surface, Polycoat Products PC-260 or a mixture of Polyprime
Due to its aromatic composition, Polyeuro® 5502F will tend 21 and sand should be used as a repair agent for cracks, spalls, bug
to yellow or darken in color and will become flat after expo- holes and voids. Upon full cure of the repair agent, prime the entire
sure to UV light. Polyeuro® 5502F may be topcoated with surface intended for coating.
an aliphatic polyurethane/polyurea coating for a colorfast Concrete Surface Preparation Reference:
finish. ASTM D4258 - Standard practice for cleaning concrete
ASTM D4259 - Standard practice for abrading concrete
PACKAGING ASTM D4260 - Standard practice for etching concrete
10 gallon kit: One 5 gallon pail of Part-A and one 5 gallon pail ASTM F1869 - Standard test method for measuring moisture vapor
of Part-B. emission rate of concrete ICRI 03732 - Concrete surface preparation.

100 gallon kit: One 50 gallon drum of Part-A and one 50 gallon
drum of Part-B.

COVERAGE
Polyeuro® 5502F may be applied at any rate to achieve
desired thickness. Theoretical coverage for 1 mil thickness
is one gallon per 1600 sq. ft.